1、膜厚不夠：處理的方法是查驗陽端氧化工藝是不是標(biāo)準(zhǔn)，看溫度，工作電壓，導(dǎo)電性等要素是不是平穩(wěn)，若有出現(xiàn)異常，請相對調(diào)節(jié)標(biāo)準(zhǔn)之，如果沒有出現(xiàn)異常，可適度增加空氣氧化時間，確保膜厚合格。
1. Insufficient film thickness: the treatment method is to check whether the oxidation process at the positive end is standard and whether the temperature, working voltage, conductivity and other factors are stable. If there is any abnormality, please adjust the standard relatively. If there is no abnormality, the air oxidation time can be increased appropriately to ensure that the film thickness is qualified.
2、染液ph值太高：這時，能用冰醋酸將ph值調(diào)為標(biāo)準(zhǔn)值。
2. The pH value of dyeing solution is too high: at this time, the pH value can be adjusted to the standard value with glacial acetic acid.

3、空氣氧化后鋼件在不銹鋼水槽中置放時間長時間：倡導(dǎo)立即染色劑，假如這種情況早已產(chǎn)生，可將鋼件放到陽端處理槽中或氰化鈉中合槽中適度解決后再開展染色劑，實際效果會非常好。
3. After air oxidation, the steel parts are placed in the stainless steel tank for a long time: it is advocated to immediately dye. If this situation has already occurred, the steel parts can be put into the positive end treatment tank or sodium cyanide joint tank for appropriate solution, and then carry out the dye. The actual effect will be very good.
4、采用染劑已溶解或發(fā)霉：這時需拆換染劑，采用適合染劑。
4. The dye has been dissolved or moldy: at this time, it is necessary to remove and replace the dye and use a suitable dye.
5、空氣氧化溫度過低，造成皮膜高密度：可適度提升空氣氧化溫度。
5. The air oxidation temperature is too low, resulting in high film density: it can moderately increase the air oxidation temperature.
6、導(dǎo)電性欠佳：將會陽端銅桿或負端鉛板松動圖示大批量導(dǎo)電性欠佳。留意清理陽端銅桿及負端鉛板，確保導(dǎo)電性。
6. Poor conductivity: the copper rod at the positive end or the lead plate at the negative end will be loose. As shown in the figure, the conductivity of a large number is poor. Pay attention to cleaning the copper rod at the positive end and the lead plate at the negative end to ensure excellent conductivity.