鋁板在生產(chǎn)過(guò)程中往往會(huì)有很多問(wèn)題，鋁板生產(chǎn)中為常見(jiàn)的問(wèn)題不外乎表面問(wèn)題、板型問(wèn)題、軋制厚度問(wèn)題。所以生產(chǎn)人員在鋁板生產(chǎn)中要時(shí)刻的關(guān)注以上幾個(gè)要點(diǎn)，下面鋁板生產(chǎn)廠家來(lái)講講吧。
There are often many problems in the production process of aluminum plates. The common problems in aluminum plate production are nothing more than surface problems, plate shape problems, and rolling thickness problems. Therefore, the production personnel should always pay attention to the above points in the aluminum plate production. Let's talk about it from the aluminum plate manufacturer.
鋁板生產(chǎn)中的表面問(wèn)題：
Surface problems in aluminum plate production:
表面問(wèn)題主要為擦劃傷、黃油斑問(wèn)題，鋁板在生產(chǎn)過(guò)程中如果機(jī)臺(tái)上面有金屬顆粒那么會(huì)在生產(chǎn)過(guò)程中出現(xiàn)紋理一直的擦劃傷，生產(chǎn)人員需要立即停機(jī)清理機(jī)臺(tái)。黃油斑問(wèn)題是由于軋制油沒(méi)有及時(shí)更換或者是軋制設(shè)備的吹風(fēng)系統(tǒng)出現(xiàn)故障導(dǎo)致的，雖然后期可通過(guò)鋁板拉彎矯清洗進(jìn)行處理，但是生產(chǎn)人員還是需要注意黃油斑，如果對(duì)于高要求的外觀件對(duì)于黃油斑都是視為不合格的鋁板。
The surface problems are mainly scratches and grease stains. If there are metal particles on the machine table during the production process, the aluminum plate will be scratched all the time during the production process. The production personnel need to stop the machine immediately to clean the machine table. The problem of grease stain is caused by the rolling oil not being replaced in time or the failure of the air blowing system of the rolling equipment. Although it can be handled through the aluminum plate stretching, bending, straightening and cleaning in the later stage, the production personnel still need to pay attention to the yellow oil stain. If the parts with high requirements for appearance are regarded as unqualified aluminum plates for the grease stain.
鋁板生產(chǎn)中的板型問(wèn)題：
Plate type problems in aluminum plate production:
板型問(wèn)題一直是比較難以控制的，主要和軋機(jī)軋輥有關(guān)系，軋機(jī)如果在長(zhǎng)期軋制過(guò)程中沒(méi)有及時(shí)修復(fù)軋輥磨損的間隙則會(huì)出現(xiàn)板型波浪問(wèn)題，中浪和邊浪都可能會(huì)產(chǎn)生。波浪板型問(wèn)題已經(jīng)發(fā)現(xiàn)生產(chǎn)人員需要立即向生產(chǎn)主任反饋，排除是否因?yàn)檐垯C(jī)壓力不均勻還是其它原因，如果是軋輥磨損嚴(yán)重需要更換軋輥。
The plate shape problem is always difficult to control, which is mainly related to the rolling mill roll. If the rolling mill fails to repair the gap of the roll wear in a timely manner during the long-term rolling process, the plate shape wave problem will occur, and the middle wave and side wave may occur. The problem of wavy plate shape has been found that the production personnel need to report it to the production director immediately to rule out whether it is due to uneven rolling mill pressure or other reasons. If the roll is seriously worn, it needs to be replaced.

鋁板生產(chǎn)中的厚度問(wèn)題：
Thickness problem in aluminum plate production:
還是和軋機(jī)有關(guān)系，軋機(jī)壓力不均勻?qū)е?，目前軋機(jī)都有在線測(cè)量設(shè)備，該問(wèn)題已經(jīng)不再經(jīng)常出現(xiàn)。
It is still related to the rolling mill, which is caused by uneven rolling mill pressure. At present, the rolling mill has online measuring equipment, and this problem no longer occurs frequently.
鋁板硬度問(wèn)題：
Hardness of aluminum plate:
主要和退火時(shí)間有關(guān)系，很多時(shí)候由于退火時(shí)間不足導(dǎo)致力學(xué)性能不達(dá)標(biāo)，比如半硬狀態(tài)的鋁板出現(xiàn)折彎開(kāi)裂，或者拉伸鋁板出現(xiàn)拉伸開(kāi)裂均是鋁板硬度不達(dá)標(biāo)，主要需要檢查退火設(shè)備的溫度、退火時(shí)間。
It is mainly related to the annealing time. In many cases, the mechanical properties are not up to the standard due to insufficient annealing time. For example, bending cracks occur on semi hard aluminum plates, or tensile cracks occur on stretched aluminum plates. The hardness of aluminum plates is not up to the standard. It is mainly necessary to check the temperature and annealing time of the annealing equipment.
生產(chǎn)車(chē)間的人員需要在生產(chǎn)中及時(shí)發(fā)現(xiàn)問(wèn)題，同時(shí)及時(shí)糾正問(wèn)題，避免鋁板出現(xiàn)質(zhì)量不合格，提高鋁板的成品率和良品率。更多相關(guān)事項(xiàng)就來(lái)我們網(wǎng)站http://www.liyukeji.com進(jìn)行咨詢(xún)吧！
The personnel in the production workshop need to find problems in time during production and correct them in time to avoid unqualified aluminum plates and improve the yield and yield of aluminum plates. Come to our website for more information http://www.liyukeji.com Consult!