The storage environment for aluminum plates should be dry, bright, well ventilated, and free from corrosive weather.

2.鋁卷應(yīng)盡量避開漏雨，雪的地方。

2. Aluminum coils should be avoided as much as possible in areas where there is rain or snow leakage.

3.加強(qiáng)軋制油的管理，其含水量控制在百分之零點(diǎn)零四以下。

3. Strengthen the management of rolling oil, and control its water content below 0.04%.

4.鋁卷的包裝應(yīng)采用密封包裝，同時每卷應(yīng)放入適量的干燥劑。

4. The packaging of aluminum coils should be sealed, and an appropriate amount of desiccant should be added to each coil.

5.由低溫區(qū)運(yùn)入溫度高，濕度大的地區(qū)時，不要立即開啟密封包裝。

5. When transporting from a low-temperature area to an area with high temperature and humidity, do not immediately open the sealed packaging.

6.包裝箱的木軸，箱板的濕度不大于18%，包裝彩色鋁卷的溫度不大于45℃，鋁卷。

6. The humidity of the wooden shaft and board of the packaging box shall not exceed 18%, and the temperature of the colored aluminum coil for packaging shall not exceed 45 ℃.

7.鋁卷在貯存時，嚴(yán)禁與化學(xué)材料和潮濕性材料一同存放。

7. When storing aluminum coils, it is strictly prohibited to store them together with chemical and humid materials.

鋁卷是一種常見的金屬產(chǎn)品，這種產(chǎn)品在工業(yè)上是有很大的需求量的，鋁卷在工業(yè)上的主要的角色是原材料，需要經(jīng)過各種各樣的加工之后，才能在市場上流通，鋁卷在市場上的規(guī)格以及型號也是非常的豐富的，基本上的需求都是能夠被滿足的，鋁卷在市場上的市場上也是有很多。

Aluminum coil is a common metal product with a high demand in industry. The main role of aluminum coil in industry is raw materials, which require various processing before being circulated in the market. The specifications and models of aluminum coil in the market are also very diverse, and the basic demand can be met. There are also many aluminum coils in the market.

如果鋁卷是放在木箱里面的，那么我們要保證木箱的濕度要小于18%，鋁卷而且鋁卷的溫度不能高于45℃。

If the aluminum coil is placed inside a wooden box, we need to ensure that the humidity of the wooden box is less than 18%, and the temperature of the aluminum coil cannot exceed 45 ℃.

如果在放置期間突然由低溫區(qū)域轉(zhuǎn)到高溫區(qū)域，那么我們不要立即將包裝打開，因?yàn)檫@樣很容易出現(xiàn)氧化的情況，我們應(yīng)該等到鋁卷適用之后在進(jìn)行拆封，這樣就不會出現(xiàn)氧化的情況。

If the packaging suddenly shifts from a low temperature area to a high temperature area during placement, we should not immediately open it because it is prone to oxidation. We should wait until the aluminum coil is suitable before unpacking, so that oxidation will not occur.

鋁卷板在生產(chǎn)過程中會出現(xiàn)各種各樣的質(zhì)量問題，造成質(zhì)量問題的原因是什么。

Various quality problems may occur during the production process of aluminum coil plates, and what are the reasons for these quality problems.

1，非金屬壓入。

1. Non metallic pressing.

主要原因：軋制工序設(shè)備條件不清凈，軋制工藝潤滑劑不清靜，工藝潤滑劑噴射壓力不足，板坯表面有擦劃傷。

Main reasons: Unclean rolling process equipment conditions, unclear rolling process lubricants, insufficient spraying pressure of process lubricants, and scratches on the surface of the slab.

2，擦傷。

2. Scratches.

主要原因：板，帶在加工生產(chǎn)過程中與導(dǎo)路，設(shè)備接觸時，產(chǎn)生相對摩擦而造成擦傷，冷軋卷端面不齊正，在立式爐退火翻轉(zhuǎn)時產(chǎn)生錯動，層與層之間產(chǎn)生擦傷，冷軋時張力不當(dāng)，開卷時產(chǎn)生層間錯動而產(chǎn)生擦傷，精整驗(yàn)收或包裝操作不當(dāng)產(chǎn)生板間滑動而造成擦傷。

Main reasons: When the plates and strips come into contact with the guide and equipment during the processing and production process, they generate relative friction and cause scratches. The end face of the cold rolled coil is not aligned, causing misalignment during annealing and flipping in a vertical furnace, causing scratches between layers. Improper tension during cold rolling, causing interlayer misalignment and scratches during uncoiling, and improper finishing acceptance or packaging operations resulting in sliding between plates and scratches.

3，碰傷。

3. Collision injury.

主要原因：板，卷在搬運(yùn)或存放過程中與其他物體碰撞產(chǎn)生，板，卷在退火料架或底盤上有其他突出物頂撞而產(chǎn)生，鋁卷。

The main reason is that the plate or coil collides with other objects during transportation or storage, and other protrusions collide with the annealing material rack or chassis, resulting in aluminum coils.